JARGAL® M RTS
Void-free, fully ground, electrofused 95% alumina (alpha-beta alumina)
The best possible glass contact properties to reduce risk of glass defects. Complete surface grinding with high surface quality.
Only available in void-free quality.
Typical application
The void-free, fully ground, electrofused 95% alumina (alpha-beta alumina), JARGAL® M RTS solution is used in end zones with extremely high quality requirements:
- spout lips and channels in float glass furnaces
- feeders for high quality glass
Chemical and physical properties
Microstructure
Typical chemical composition
Typical crystallographic analysis
Physical characteristics
Description | International standards | British standards |
---|---|---|
Refractoriness under load of 2.105 Pa | 1,750°C | 3,182°F |
Cold crushing strength | >200Mpa | >29,007psi |
Typical bulk density | 3.4g/cm3 | 212pcf |
Storage
The void-free, fully ground, electrofused 95% alumina (alpha-beta alumina), JARGAL® M RTS solution must be stored in a dry environment protected from weather conditions.
Related products
Void-free, electrofused 95% alumina (alpha-beta alumina)
Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
Void-free structure enabling longer lifetime.
Void-free, electrofused 95% alumina (alpha-beta alumina) tiles
Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
Void-free structure enabling longer lifetime.
Regular cast, electrofused 95% alumina (alpha-beta alumina)
Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
Alumina cement for bottom solutions
Alumina cement to seal and joint Alumina surfaces.
Sintered mullite 68% alumina
Good glass contact properties and thermal shock resistance. Low iron oxide content. Available in complex and large shapes.
Void-free electrofused alumina-zirconia-silica (AZS) with 40% zirconia solution
Alumina-zirconia-silica (AZS) material with highest corrosion resistance and good castability for various shapes and sizes. It is essentially free of casting cavities and allows a very homogeneous internal structure and corrosion resistance.