MONOFRAX® CS-3 Epic-3 & DCL

Fused cast

Void-free electrofused alumina-zirconia-silica (AZS) with 34% zirconia

Alumina-zirconia-silica (AZS) with good castability enabling complex and varied shapes and sizes. Void-free structure enabling longer lifetime.
DCL grade apply typically for thickness below 150 mm (6"").
This product is exclusively produced at the Falconer, NY, USA plant.
Equivalent to ER 1681 RT solution.

Typical application Chemical and Physical Properties Storage
Fused cast

Typical application

The void-free electrofused alumina-zirconia-silica (AZS) with 34% zirconia, MONOFRAX® CS-3 Epic-3 & DCL provide a high corrosion resistance for a very large range of applications:

  • superstructures, including crowns
  • glass-contact working end and feeders for sodalime and insulation glass fiber

Chemical and Physical Properties

Microstructure

Microstructure monofrax CS-3 Epic-3

Typical Chemical Composition

 
 

Physical characteristics

Description International standards British standards
Refractoriness under load of 2.105 Pa (2kg/cm²) 1,700°C 3,092°F
Cold crushing strength ≥350Mpa ≥50,763psi
Typical bulk density 3.70g/cm3 231pcf

Storage

The void-free structure of the MONOFRAX® CS-3 Epic-3 & DCL must be stored in a dry environment protected from weather conditions.

Related products

Fused cast

MONOFRAX® M RC

Regular cast electrofused with 94% alumina (alpha-beta alumina)

Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
This product is exclusively produced at the Falconer, NY, USA plant.
Equivalent to JARGAL® M RN solution.

Go to product
Fused cast

JARGAL® M RT

Void-free, electrofused 95% alumina (alpha-beta alumina)

Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
Void-free structure enabling longer lifetime.

Go to product
Fused cast

JARGAL® M RTS

Void-free, fully ground, electrofused 95% alumina (alpha-beta alumina)

The best possible glass contact properties to reduce risk of glass defects. Complete surface grinding with high surface quality.
Only available in void-free quality.

Go to product
Fused cast

JARGAL® M RT DALLE

Void-free, electrofused 95% alumina (alpha-beta alumina) tiles

Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
Void-free structure enabling longer lifetime.

Go to product
Monolithics

ERGAL® SL CAST

Alumina monolithic bottom solution

Self levelling high-purity alumina concrete safety sublayer with excellent glass contact properties.

Go to product
Monolithics

ERGAL® 05 CEMENT

Alumina cement for bottom solutions

Alumina cement to seal and joint Alumina surfaces.

Go to product