MONOFRAX® M DCL

Range
Fused cast
Subtitle

Void-free electrofused with 94% alumina (alpha-beta alumina)

Description

Excellent glass contact properties with an extremely low defect potential.
High resistance to alkali vapor and creep for superstructure application.
Void-free structure enabling a longer service life. 
This product is exclusively produced at the Falconer, NY, USA plant.
Equivalent to JARAL®M RT solution.

Typical application

Available in various shape and size, the void-free electrofused with 94% alumina (alpha-beta alumina), MONOFRAX® M DCL solution is used in a very large range of applications, specifically in areas sensitive to glass defect generation:

  • glass-contact working end, feeders and canals
  • superstructures, crowns
     

Chemical and Physical Properties

Microstructure

Image
Microstructure M DCL

Typical Chemical Composition

 
 

Physical Characteristics

Description International standards British standards
Refractoriness under load of 2.105 Pa 1,750°C 3,182°F
Cold crushing strength >200Mpa >29,007psi
Typical bulk density 3.17g/cm3 198pcf

Storage

The void-free electrofused with 94% alumina (alpha-beta alumina) solution must be stored in a dry environment protected from weather conditions.

Related products

Fused cast

MONOFRAX® M RC

Regular cast electrofused with 94% alumina (alpha-beta alumina)

Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
This product is exclusively produced at the Falconer, NY, USA plant.
Equivalent to JARGAL® M RN solution.

Fused cast

JARGAL® M RT

Void-free, electrofused 95% alumina (alpha-beta alumina)

Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
Void-free structure enabling longer lifetime.

Fused cast

JARGAL® M RTS

Void-free, fully ground, electrofused 95% alumina (alpha-beta alumina)

The best possible glass contact properties to reduce risk of glass defects. Complete surface grinding with high surface quality.
Only available in void-free quality.

Fused cast

JARGAL® M RT DALLE

Void-free, electrofused 95% alumina (alpha-beta alumina) tiles

Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
Void-free structure enabling longer lifetime.

Monolithics

ERGAL® SL CAST

Alumina monolithic bottom solution

Self levelling high-purity alumina concrete safety sublayer with excellent glass contact properties.

Monolithics

ERGAL® 05 CEMENT

Alumina cement for bottom solutions

Alumina cement to seal and joint Alumina surfaces.