MONOFRAX® CS-3 DCL tile

Range
Fused cast
Subtitle

Void-free electrofused alumina-zirconia-silica (AZS) tiles with 34% zirconia

Description

Alumina-zirconia-silica (AZS) tiles solutions for paving applications with a wide range of sizes.
This product is exclusively produced at the Falconer, NY, USA plant.
Equivalent to ER 1681 RTD solution.

Typical application

The void-free electrofused alumina-zirconia-silica (AZS) tiles with 34% zirconia, MONOFRAX® CS-3 DCL tile provides a high corrosion resistance for a very large range of applications:

  • bottom glass contact
  • patching and sidewall back up

MONOFRAX® CS-3 DCL tile is available in standard thicknesses of 75mm (3"), 100mm (4"), 125mm (5"), 150mm (6") and 175mm (7").

 

Chemical and Physical Properties

Microstructure

Image
Microstructure

 

Typical chemical composition

 

Physical characteristics

Description International standards British standards
Refractoriness under load of 2.105 Pa (2kg/cm²) 1,700°C 3,092°F
Cold crushing strength ≥350Mpa ≥50,763psi
Typical bulk density 3.68g/cm3 230pcf

Storage

The void-free electrofused alumina-zirconia-silica (AZS) tiles with 34% zirconia must be must be stored in a dry environment protected from weather conditions.

Related products

Fused cast

Void-free electrofused Alumina-Zirconia-Silica (AZS) tiles with 32% zirconia

Alumina-Zirconia-Silica (AZS) paving with fully ground joint faces for tight joint application.

Fused cast

Void-free electrofused Alumina-Zirconia-Silica (AZS) tiles with 32% zirconia

Alumina-Zirconia-Silica (AZS) for paving applications with a wide range of sizes

Fused cast

Void-free electrofused Alumina-zirconia-silica (AZS) tiles with 39% yttria-doped zirconia

Alumina-zirconia-silica (AZS) for paving applications with a wide range of sizes. The only AZS allowing joint closure at operating conditions.

Sintered

Bonded alumina-zirconia-silica (AZS) with 30% zirconia

Made of alumina-zirconia-silica (AZS) grains. High resistance to glass corrosion. Available in large format with large range of thickness.