ER 2010 RIC RTD

Range
Fused cast
Subtitle

Void-free electrofused Alumina-zirconia-silica (AZS) tiles with 39% yttria-doped zirconia

Description

Alumina-zirconia-silica (AZS) for paving applications with a wide range of sizes. The only AZS allowing joint closure at operating conditions.

Typical application

  • bottom glass contact
  • patching and sidewall back up

It is specifically dedicated to bottoms in clear and extraclear glass furnaces (reduced iron content), allowing significant reduction of low-temperature blistering.

The void-free electrofused Alumina-zirconia-silica (AZS) tiles with 39% yttria-doped zirconia, ER 2010 RIC RTD  solution is available in standard thicknesses of 75, 100, 120 and 150mm.
 

Read Technical Article

Chemical and physical properties

Microstructure

Image
Microstructure of ER 2010 RIC

Typical chemical composition

 

Typical crystallographic analysis

 

Physical characteristics

DescriptionInternational standardsBritish standards
Refractoriness under load of 2.105 Pa1,700°C3,092°F
Cold crushing strength≥350Mpa≥50,763psi
Typical bulk density4.0g/cm3250pcf

Thermal conductivity curve

Thermal conductivity curve fused cast ER 2010 RIC RTD

Storage

The void-free electrofused Alumina-zirconia-silica (AZS) tiles with 39% yttria-doped zirconia must be stored in a dry environment protected from weather conditions. 

Related products

Fused cast

Void-free electrofused alumina-zirconia-silica (AZS) with 39% yttria-doped zirconia

The alumina-zirconia-silica (AZS) material with the highest corrosion resistance for simple rectangular shapes. The only AZS allowing joint closure at operating conditions.

Fused cast

Void-free electrofused alumina-zirconia-silica (AZS) with 40% zirconia solution

Alumina-zirconia-silica (AZS) material with highest corrosion resistance and good castability for various shapes and sizes. It is essentially free of casting cavities and allows a very homogeneous internal structure and corrosion resistance.

Fused cast

Void-free electrofused alumina-zirconia-silica (AZS) with 36% zirconia

High corrosion resistance alumina-zirconia-silica (AZS) for simple rectangular shapes. Essentially free of casting cavity which allows a very homogeneous internal structure and corrosion resistance.