S-CEMENT

Range
Monolithics
Subtitle

Alumina-zirconia-silica (AZS) cement for bottom solutions

Description

Alumina-zirconia-silica (AZS) cement ensures the flatness before ER 1681® paving tiles installation.

Typical application

Bedding cement for ER 1681 DALLE TJ or ER 1681 RTD paving tiles with stiff consistency allowing a leveling thickness from 3 mm to 10mm.

S-CEMENT's high zirconia content provides an excellent corrosion resistance.

Chemical and physical properties

Typical chemical composition

 

Typical crystallographic analysis

  • corundum
  • monoclinic zirconia

Physical characteristics

Description International standards British standards
Maximum diameter 0.5mm 35Mesh
Typical bulk density 3g/cm3 187pcf

Instructions of use

  • Hydraulic setting
  • Typical drinkable water addition: 13%-15% by weight

Packaging and storage

  • 25kg bag
  • Must be properly stored up to expiry date in undamaged original sealed packaging, in dry conditions at temperatures between +5°C and +40°C

Related products

Monolithics

Alumina monolithic bottom solution

Self levelling high-purity alumina concrete safety sublayer with excellent glass contact properties.

Fused cast

Void-free electrofused Alumina-Zirconia-Silica (AZS) tiles with 32% zirconia

Alumina-Zirconia-Silica (AZS) paving with fully ground joint faces for tight joint application.

Fused cast

Void-free electrofused Alumina-zirconia-silica (AZS) tiles with 39% yttria-doped zirconia

Alumina-zirconia-silica (AZS) for paving applications with a wide range of sizes. The only AZS allowing joint closure at operating conditions.

Fused cast

Void-free electrofused Alumina-Zirconia-Silica (AZS) tiles with 32% zirconia

Alumina-Zirconia-Silica (AZS) for paving applications with a wide range of sizes

Fused cast

Void-free electrofused alumina-zirconia-silica (AZS) with 40% zirconia solution

Alumina-zirconia-silica (AZS) material with highest corrosion resistance and good castability for various shapes and sizes. It is essentially free of casting cavities and allows a very homogeneous internal structure and corrosion resistance.