T1186
Sintered dense tin oxide
High electrical conductivity. High corrosion resistance with excellent glass contact properties.
Typical application
T1186 electrodes are used for electrical boosting or direct melting. Available in large size with rectangular or cylindrical cross section.
Homogenous structure enabling a uniform electrical resistivity.
Chemical and physical properties
Microstructure
Typical chemical composition
Typical crystallographic analysis
Main phase:
- stannic oxide
Physical characteristics
Description | International standards | British standards |
---|---|---|
Cold modulus of rupture | 45Mpa | 6,527psi |
Cold crushing strength | 193Mpa | 27,992psi |
Apparent porosity | 5% | 5% |
Typical bulk density | 6.5g/cm3 | 406pcf |
Storage
The sintered dense tin oxide, Z1186 solution must be stored in a dry environment protected from weather conditions.
Related products
Sintered dense tin oxide
High electrical conductivity. Very high corrosion resistance with excellent glass contact properties.
Sintered dense tin oxide
High electrical conductivity. High corrosion resistance with excellent glass contact properties.
Void-free electrofused zirconia with improved high electrical resistivity
Excellent corrosion resistance and glass contact properties combined with a very high and stable electrical resistivity while providing the lowest potential for seed and blister formation.
Void-free electrofused 94% zirconia
Excellent corrosion resistance and glass contact properties with the lowest potential for seed and blister formation.