T1187 LC

Range
Sintered
Subtitle

Sintered dense tin oxide

Description

High electrical conductivity. High corrosion resistance with excellent glass contact properties.

Typical application

Very low porosity T1187 LC electrodes are used for direct melting of special glasses with very specific optical properties. Available in large size with rectangular or cylindrical cross section.

Homogenous structure enabling a uniform electrical resistivity.

Chemical and physical properties

Microstructure

Image
T1187 LC microstructure

Typical chemical composition

 

Typical crystallographic analysis

Main phase:

  • stannic oxide

Physical characteristics

Description International standards British standards
Cold modulus of rupture 48Mpa 6,962psi
Cold crushing strength 317Mpa 45,977psi
Apparent porosity 2.5% 2.5%
Typical bulk density 6.6g/cm3 412pcf

Electrical resistivity curve

Electrical resistivity curve sintered T1187 LC

Storage

The sintered dense tin oxide, T1187 LC solution must be stored in a dry environment protected from weather conditions.

Related products

Sintered

Sintered dense tin oxide

High electrical conductivity. High corrosion resistance with excellent glass contact properties.

Sintered

Sintered dense tin oxide

High electrical conductivity. Very high corrosion resistance with excellent glass contact properties.

Fused cast

Void-free electrofused zirconia with improved high electrical resistivity

Excellent corrosion resistance and glass contact properties combined with a very high and stable electrical resistivity while providing the lowest potential for seed and blister formation.

Fused cast

Void-free electrofused 94% zirconia

Excellent corrosion resistance and glass contact properties with the lowest potential for seed and blister formation.