MONOFRAX® CS-3 RC

Fused cast

Regular cast electrofused alumina-zirconia-silica (AZS) with 34% zirconia

Good castability Alumina-zirconia-silica (AZS) enabling complex and varied shapes and sizes.
This product is exclusively produced at the Falconer, NY, USA plant.
Equivalent to ER 1681 RN solution.

Typical Application Chemical and Physical Properties Storage
Fused cast

Typical Application

The regular cast electrofused alumina-zirconia-silica (AZS) with 34% zirconia, MONOFRAX® CS-3 solution, is used in a very large range of applications:

  • superstructures, including crowns
  • glass-contact working end and feeders for sodalime and insulation glass fiber

Chemical and Physical Properties

Microstructure

Microstructure

Typical Chemical Composition

 
 

Physical characteristics

Description International standards British standards
Refractoriness under load of 2.1055 Pa (2kg/cm²) 1,700°C 3,092°F
Cold crushing strength 331Mpa 48,000psi
Typical bulk density 3.44g/cm3 215pcf

Storage

The regular cast electrofused alumina-zirconia-silica (AZS) with 34% zirconia, MONOFRAX® CS-3 solution must be stored in a dry environment protected from weather conditions.

Related products

Fused cast

ER 1681® RN

Regular cast, electrofused Alumina-Zirconia-Silica (AZS) with 32% zirconia

Good castability Alumina-Zirconia-Silica (AZS) enabling complex and varied shapes and sizes.

Go to product
Fused cast

MONOFRAX® CS-3 Epic-3 & DCL

Void-free electrofused alumina-zirconia-silica (AZS) with 34% zirconia

Alumina-zirconia-silica (AZS) with good castability enabling complex and varied shapes and sizes. Void-free structure enabling longer lifetime.
DCL grade apply typically for thickness below 150 mm (6"").
This product is exclusively produced at the Falconer, NY, USA plant.
Equivalent to ER 1681 RT solution.

Go to product
Fused cast

MONOFRAX® CS-3 DCL tile

Void-free electrofused alumina-zirconia-silica (AZS) tiles with 34% zirconia

Alumina-zirconia-silica (AZS) tiles solutions for paving applications with a wide range of sizes.
This product is exclusively produced at the Falconer, NY, USA plant.
Equivalent to ER 1681 RTD solution.

Go to product
Fused cast

ER 1851 RN LOWEX®

Regular cast electrofused Alumina-Zirconia-Silica (AZS) with 36% zirconia and a low silicate phase (14%)

Low exudation and high creep resistance.
Good resistance to alkali vapour and carry over.

Go to product