BP MULLITE
Sintered fused mullite 75% alumina
Made of fused mullite grains. High creep resistance with excellent vapour corrosion resistance.
Typical application
BP MULLITE is dedicated to superstructure application. Due to its high creep resistance at very high temperature, BP MULLITE is used in crowns and feeder covers for reinforcement and textile fiber glass furnaces as well as for vitroceramic, borosilicate and sodium silicate glass furnaces.
For very heavy insulation crown application, refer to BP MULLITE REC.
If mortar is required, use BP MULLITE MORTAR.
Chemical and physical properties
Microstructure
Typical chemical composition
Typical crystallographic analysis
Main phase: mullite
Secondary phase: corundum + silicate
Physical characteristics
Description | International standards | British standards |
---|---|---|
Refractoriness under load 0.2Mpa at 0.5% | 1,700°C | 3,092°F |
Cold crushing strength | 100Mpa | 14,504si |
Coefficient of thermal expansion | 5.4 10-6K-1 | 3 10-6°F-1 |
Thermal conductivity at 1,000°C | 2 W.m-1.K-1 | 13.8 BTU in hr-1ft-2°F-1 |
Creeping at 1,700°C under load 0.4Mpa 0-100h | 2% | 2% |
Porosity | 15% | 15% |
Typical bulk density | 2.7g/cm3 | 168.5pcf |
Storage
The sintered fused mullite 75% alumina, BP MULLITE solution must be stored in a dry environment protected from weather conditions.
Related products
Sintered fused mullite 75% alumina
Made of fused mullite grains. Excellent creep resistance with vapour corrosion resistance at very high temperatures.
Void-free, electrofused 95% alumina (alpha-beta alumina)
Excellent glass contact properties with extremely low defect potential.
High resistant to alkali vapor and creep for superstructure application.
Void-free structure enabling longer lifetime.
Mullite-based jointing mortar
Mullite mortar for high temperature superstructure application.
Void-free electrofused alumina-zirconia-silica (AZS) with 36% zirconia and a low silicate phase (14%)
Low exudation and high creep resistance alumina-zirconia-silica (AZS).
Good resistance to alkali vapours and carry over.
Void-free structure enabling longer lifetime.
Sintered mullite 67% alumina
High corrosion resistance to alkali vapours. Excellent creep resistance. Available in complex and large shapes.
Sintered sillimanite 61% alumina
Excellent thermal shock resistance. Available in complex and large shapes.
Bonded alumina-zirconia-silica (AZS) with 30% zirconia
Made of alumina-zirconia-silica (AZS) grains. High corrosion resistance to alkali or boron vapours. Available in complex and large shapes.
Sintered mullite 75% alumina
Good corrosion resistance to alkali vapours. Available in standard brick format.