ZIRCHROM 30
Sintered 30% chrome-alumina and alumina-zirconia-silica (AZS)
Good corrosion and thermal shock resistance.
Typical application
ZIRCHROM 30 is mainly used for glass contact and superstructure application for insulation glass furnaces.
For crown application, refer to ZIRCHROM HC.
Also a potential material for overcoating applications.
Chemical and physical properties
Typical chemical composition
Typical crystallographic analysis
- Cr2O3 - Al2O3 solid solution
- Corundum
- Monoclinic zirconia
Physical characteristics
Description | International standards | British standards |
---|---|---|
Cold crushing strength | 160MPa | 23,206psi |
Coefficient of thermal expansion at 1,000°C | 8 10-6°C | 4.4 10-6°F-1 |
Thermal conductivity at 1,000°C | 1.7 W.m-1.K-1 | 11.8 BTU in hr-1ft-2°F-1 |
Open porosity | 16% | 16% |
Typical bulk density | 3.4g/cm3 | 212pcf |
Storage
The sintered 30% chrome-alumina and alumina-zirconia-silica (AZS), ZIRCHROM 30 solution must be stored in a dry environment protected from weather conditions.
Related products
Sintered 50% chrome-alumina and alumina-zirconia-silica (AZS)
High corrosion resistance.
Sintered 30% chrome-alumina
High creep resistance with low chrome sublimation level. Good resistance to vapour environment.
Sintered 85% high chrome
Very high corrosion resistance with high thermal-mechanical properties.
Sintered 30% chrome-alumina
High electrical resistivity. Good corrosion and thermal shock resistance.