ZMV
Sintered zircon-mullite with 20% zirconia
Made of fused zircon-mullite grains. High resistance to vapours corrosion. Available in complex and large shapes.
Typical application
ZMV is manufactured with zircon-mullite fused grains providing a high corrosion resistance to alkali vapours. Used in forehearth superstructure subject to high corrosion such as sodalime coloring zone or soda-lime extra white glass.
Refer to ZMP for application in standard brick format.
Chemical and physical properties
Typical chemical composition
Typical crystallographic analysis
Main phase:
- corundum
- mullite
- baddeleyite
Physical characteristics
Description | International standards | British standards |
---|---|---|
Refractoriness under load of 0.2Mpa at 0.5% | 1550°C | 2822°F |
Cold crushing strength | 80Mpa | 11,603psi |
Apparent porosity | 19% maximum | 19% maximum |
Typical bulk density | 3.1g/cm3 | 194pcf |
Storage
The sintered zircon-mullite with 20% zirconia, ZMV solution must be stored in a dry environment protected from weather conditions.
Related products
Sintered zircon-mullite with 20% zirconia
Made of fused zircon-mullite grains. High resistance to vapours corrosion. Available in standard brick format.
Bonded alumina-zirconia-silica (AZS) with 30% zirconia
Made of alumina-zirconia-silica (AZS) grains. High resistance to glass corrosion. Available in large format with large range of thickness.
Bonded alumina-zirconia-silica (AZS) with 30% zirconia
Made of alumina-zirconia-silica (AZS) grains. High corrosion resistance to alkali or boron vapours. Available in complex and large shapes.
Bonded alumina-zirconia-silica (AZS) with 30% zirconia
Made of alumina-zirconia-silica (AZS) grains. High corrosion resistance to alkali or boron vapours. Available in complex and large shapes.
Sintered alumina-zirconia-silica (AZS) with 30% zirconia
Made of alumina-zirconia-silica (AZS) grains. Good resistance to vapours corrosion. Available in standard brick format.
Sintered zircon with 66% zirconia
Zirconium silicate. Very high resistance to vapours corrosion. Available in standard brick format.