ERSOL® 06 CEMENT
Alumina-zirconia-silica (AZS) cement for bottom solutions
Alumina-zirconia-silica (AZS) cement ensures the flatness between the ERSOL® cast solutions and the ER 1681® tile paving.
Typical application
Easy-to-use organic setting cement to be applied on ERSOL® MAX FLOW or ERSOL® SL concrete safety layers before AZS paving installation.
Its fine grain and narrow grain size distribution ensures a uniform layer.
For vertical applications, refer to ERPLAST® 05 CEMENT.
Chemical and physical properties
Typical chemical composition
Typical crystallographic analysis
Main phase:
- corundum
- monoclinic zirconia
Physical characteristics
| Description | International standards | British standards |
|---|---|---|
| Maximum grain diameter | 0.6mm | 30Mesh |
| Typical bulk density | 3.1g/cm3 | 194pcf |
Instructions of use
Organic setting with 8% to 10% drinkable water by weight.
Instruction of use
Packaging and storage
- 25kg bag
- Must be properly stored up to expiry date in undamaged original sealed packaging, in dry conditions at temperatures between +5°C and +40°C
Related products
Alumina-zirconia-silica (AZS) cement for bottom solutions
Alumina-zirconia-silica (AZS) cement ensures the flatness before ER 1681® paving tiles installation.
Void-free electrofused Alumina-Zirconia-Silica (AZS) tiles with 32% zirconia
Alumina-Zirconia-Silica (AZS) paving with fully ground joint faces for tight joint application. Automatically fully controlled with specific Radar dedicated for thin pieces.
Void-free electrofused Alumina-zirconia-silica (AZS) tiles with 39% yttria-doped zirconia
Alumina-zirconia-silica (AZS) for paving applications with a wide range of sizes. The only AZS allowing joint closure at operating conditions.
Void-free electrofused Alumina-Zirconia-Silica (AZS) tiles with 32% zirconia
Alumina-Zirconia-Silica (AZS) for paving applications with a wide range of sizes
Void-free electrofused alumina-zirconia-silica (AZS) with 40% zirconia solution
Alumina-zirconia-silica (AZS) material with highest corrosion resistance and good castability for various shapes and sizes. It is essentially free of casting cavities and allows a very homogeneous internal structure and corrosion resistance.